Details for Patent: 6,358,533
✉ Email this page to a colleague
Title: | Pharmaceutical excipient having improved compressibility |
Abstract: | A microcrystalline cellulose-based excipient having improved compressibility, whether utilized in direct compression, dry granulation or wet granulation formulations, is disclosed. The excipient is an agglomerate of microcrystalline cellulose particles and from about 0.1% to about 20% silicon dioxide particles, by weight of the microcrystalline cellulose, wherein the microcrystalline cellulose and silicon dioxide are in intimate association with each other. The silicon dioxide utilized in the novel excipient has a particle size from about 1 nanometer to about 100 microns. Most preferably, the silicon dioxide is a grade of colloidal silicon dioxide. |
Inventor(s): | Sherwood; Bob E. (Amenia, NY), Staniforth; John H. (Bath, GB), Hunter; Edward A. (Glenham, NY) |
Assignee: | Edward Mendell, Co., Inc. (Patterson, NY) |
Filing Date: | Jan 04, 2001 |
Application Number: | 09/754,760 |
Claims: | 1. An excipient composition comprising a particulate agglomerate of microcrystalline cellulose coprocessed with from about 5.0% to about 10% by weight silicon dioxide, based on the weight of microcrystalline cellulose, said microcrystalline cellulose and silicon dioxide being in intimate association with each other and said silicon dioxide being integrated with or partially coating said microcrystalline cellulose, said silicon dioxide portion of said agglomerate being derived from a silicon dioxide having an average primary particle size from about 1 nm to about 100 .mu.m. 2. The composition of claim 1, wherein said silicon dioxide portion of said agglomerate is derived from silicon dioxide having an average primary particle size from about 5 nm to about 40 .mu.m. 3. The composition of claim 1, wherein said silicon dioxide portion of said agglomerate is derived from colloidal silicon dioxide. 4. The composition of claim 1, wherein said particulate agglomerates have an average particle size of from about 10 .mu.m to about 1,000 .mu.m. 5. The composition of claim 1, wherein said microcrystalline cellulose is coprocessed with about 5.0% by weight silicon dioxide, based on the weight of microcrystalline cellulose. 6. The composition of claim 5, wherein said silicon dioxide portion of said agglomerate is derived from silicon dioxide having an average primary particle size from about 5 nm to about 40 .mu.m. 7. The composition of claim 5, wherein said silicon dioxide portion of said agglomerate is derived from colloidal silicon dioxide. 8. The composition of claim 5, wherein said particulate agglomerates have an average particle size of from about 10 .mu.m to about 1,000 .mu.m. 9. The composition of claim 1, wherein microcrystalline cellulose is coprocessed with about 10% by weight said silicon dioxide, based on the weight of microcrystalline cellulose. 10. The composition of claim 9, wherein said silicon dioxide portion of said agglomerate is derived from silicon dioxide having an average primary particle size from about 5 nm to about 40 .mu.m. 11. The composition of claim 9, wherein said silicon dioxide portion of said agglomerate is derived from colloidal silicon dioxide. 12. The composition of claim 9, wherein said particle agglomerates have an average particle size of from about 10 .mu.m to about 1,000 .mu.m. 13. The composition of claim 1, wherein said particulate agglomerates have an average particle size of from about 10 .mu.m to about 500 .mu.m. 14. The composition of claim 1, wherein said particulate agglomerates have an average particle size of from about 30 .mu.m to about 250 .mu.m. 15. The composition of claim 1, wherein said particulate agglomerates have a moisture content from about 0.5% to about 15%. 16. The composition of claim 1, wherein said particulate agglomerates further comprise a member of the group consisting of non-silicon metal oxides, starches, starch derivatives, surfactants, polyalkylene oxides, celluloses, cellulose ethers, cellulose esters and mixtures thereof. 17. The composition of claim 1, wherein said silicon dioxide portion of said agglomerate is derived from silicon dioxide having a surface area from about 10 m.sup.2 /g to about 500 m.sup.2 /g. 18. The composition of claim 1, wherein said silicon dioxide portion of said agglomerate is derived from silicon dioxide having a surface area from about 175 m.sup.2 /g to about 350 m.sup.2 /g. 19. The composition of claim 1, wherein said excipient has a bulk density from about 0.2 g/ml to about 0.6 g/ml. 20. The composition of claim 3, wherein said excipient has a bulk density from about 0.35 g/ml to about 0.55 g/ml. 21. An excipient composition comprising a particulate agglomerate of microcrystalline cellulose coprocessed with from about 5.0% by weight silicon dioxide, based on the weight of microcrystalline cellulose, and microcrystalline cellulose and silicon dioxide being in intimate association with each other and said silicon dioxide being integrated with or partially coating said microcrystalline cellulose, said silicon dioxide portion of said agglomerate being derived from a silicon dioxide having an average primary particle size from about 1 nm to about 100 .mu.m. 22. An excipient composition comprising a particulate agglomerate of microcrystalline cellulose coprocessed with from about 10% by weight silicon dioxide, based on the weight of microcrystalline cellulose, said microcrystalline cellulose and silicon dioxide being in intimate association with each other and said silicon dioxide being integrated with or partially coating said microcrystalline cellulose, said silicon dioxide portion of said agglomerate being derived from a silicon dioxide having an average primary particle size from about 1 nm to about 100 .mu.m. |